The substructural development of martensite plates at different stage of the transformation for an Fe-21Ni-4Mn alloy has been investigated by using transmission electron microscope. Twinning was found in small thin platelets at the initial stage.Fine twins extend to the whole platelet.The dislocations and twins were found in the thick platelets at a later stage.Bending of the twins was also observed frequently at this stage.Finally,several platelets coalesce with each other to form a macroscopic(252)_f martensite“plate”.The original habit plane of the individual platelet was measured to be close to(121)_f.
关键词:
Fe-Ni-Mn alloy
,
null
,
null
GUO Chengbi ZHOU Weisheng Dalian Institute of Technology
,
Dalian
,
Liaoning
,
China Professor
,
Dept.of Shipbuilding
,
Dalian Institute of Technology
,
Dalian
,
Liaoning
,
China
金属学报(英文版)
The in-phase and out-of-phase thermal fatigue,the C-P type and P-C type isothermal fa- tigue of grey cast iron were experimentally studied.The fatigue life was evaluated analytically by using the elastic-plastic fracture mechanics method(mainly J integral).The results of ex- periments and calculations showed that the lifes of in-phase and C-P type fatigue are longer than that of out-of-phase and P-C type fatigue respectively within the same strain range. This is in contrast to the results of other materials such as low carbon steel.On the other hand, the predicted lifes are consistent with experimental results.This suggests that J integral as a mechanics parameter for characterizing the thermal fatigue strength of grey cast iron and the mechanics model and the calculation method developed here are efficient.A parameter ΔW_1 was proposed from energy aspect to characterize the capacity of crack propagation. The isothermal fatigue life is the same as the thermal fatigue life for identical ΔW_1 values.
关键词:
grey cast iron
,
null
,
null
ZHOU Jiyang Dalian University of Technology
,
Liaoning
,
ChinaW.SCHMITZ S.ENGLER Aachen Institute of Technology
,
FRG Associate Professor
,
Divisionof Foundry
,
Dalian Institute of Technology
,
Liaoning
,
China
金属学报(英文版)
To study the growth of austenitic shells around the spheroidal graphite,color metallography has been employed.It is found that the shell is not a continuous layer of austenite,but a clus- ter of wedge-shaped crystals.Three types of shells have been observed.That may strongly af- fect the deterioration of the spheroidal graphite.The mechanism of the formation of the austenitic shells has also been discussed.